Design of the Pore Structure of Sponge-Structured Cement Pastes with Both Absorption and Storage Functions

Tong Li1,2, Guojun Du1, Hefang Zhang3

  • 1Key Laboratory of Mechanical Reliability for Heavy Equipment and Large Structures of Hebei Province, Yanshan University, Qinhuangdao 066004, China.

Materials (Basel, Switzerland)
|December 31, 2025
PubMed

Keywords:
capillary water absorption performancecement pastecement-based materialsmineral admixturepore structurewater storage performance

More Related Videos

Microbiologically Induced Calcite Precipitation Mediated by Sporosarcina pasteurii09:04

Microbiologically Induced Calcite Precipitation Mediated by Sporosarcina pasteurii

Published on: April 16, 2016

22.6K
Expression of Cementitious Pore Solution and the Analysis of Its Chemical Composition and Resistivity Using X-ray Fluorescence06:27

Expression of Cementitious Pore Solution and the Analysis of Its Chemical Composition and Resistivity Using X-ray Fluorescence

Published on: September 23, 2018

9.7K

Related Concept Videos

Porosity in Cement Paste01:18

Porosity in Cement Paste

The porosity of concrete is a measure of the void spaces within its structure. These spaces impact its strength and durability significantly. When water and cement interact, a chemical reaction called hydration creates a semi-solid paste. This paste includes combined water, making up approximately 23% of the cement's dry mass, and gel water, which fills minuscule voids known as gel pores, accounting for about 28% of the cement gel volume.
The balance of water to cement in the mix is...
417
Pore Size Distribution01:23

Pore Size Distribution

In concrete, the pore size distribution significantly influences the material's properties. Capillary pores, markedly larger than gel pores, form a vast network within partially hydrated cement paste, reducing the concrete's strength and increasing its permeability. This heightened permeability leads to a greater risk of damage from environmental factors like freeze-thaw cycles and chemical attacks, with the extent of vulnerability also being tied to the water-to-cement ratio.
Adequate...
409
Porosity and Absorption of Aggregate01:20

Porosity and Absorption of Aggregate

Aggregates contain pores of varying sizes; while some are completely enclosed within the particles, others open onto the surface, allowing water to penetrate. The porosity of aggregates is a major factor contributing to the overall porosity of concrete, given that aggregates constitute about three-quarters of concrete's volume.
When all pores in an aggregate are filled with water, the aggregate is considered saturated and surface-dry. If left in dry air, water will evaporate until the...
708
Types of Cement II01:22

Types of Cement II

Portland blast-furnace cement is made by blending Portland cement clinker with granulated blast-furnace slag, which accounts for 25 to 65 percent of the cement's weight. Despite its similarities to ordinary Portland (Type I) cement in terms of fineness and setting times, its early strength is lower, though it achieves comparable strength later on. It's particularly suited for mass concrete structures and marine environments due to its lower heat of hydration and superior sulfate...
365
Hydration of Cement01:24

Hydration of Cement

Hydration of cement is a chemical reaction between cement particles and water. This process occurs primarily through two mechanisms: through-solution and topochemical. In the through-solution process, anhydrous compounds dissolve into their constituents, hydrates form in the solution, and then precipitate from the supersaturated solution. The topochemical process involves solid-state reactions at the cement particle surface. The through-solution process dominates the topochemical process at the...
757
Total Voids in Concrete01:12

Total Voids in Concrete

Total voids in concrete encompass gel water volume, capillary pores, and entrapped air. Gel water (retained within the cement hydration products) and physically entrapped or adsorbed water are significant for the hydration process. For complete hydration, it's estimated that the space needed for the products of a cubic centimeter of cement doubles. Capillary pores constitute the unoccupied space within the hydrated cement paste, with their size largely influenced by the water-to-cement...
413