Impact of EVOH, Ormocer^® Coating, and Printed Labels on the Recyclability of Polypropylene for Packaging Applications

Flexible packaging often consists of multilayer films that combine different materials to achieve high barrier performance, but these structures are incompatible with current recycling technologies. Polyolefins such as polypropylene (PP) offer more recyclable alternatives but require additional oxygen-barrier materials that do not compromise recyclability. This study investigates the influence of ethylene vinyl alcohol (EVOH), Ormocer^® barrier coating, and PP labels with different adhesives on PP recyclability. Recyclates were produced using twin-screw extruder to simulate the recycling process and then injection-molding to make tensile test specimens. Mechanical properties, melt flow rate (MFR), oxygen induction time (OIT), and odor were evaluated. Findings showed that low label content (5-12.5%) has minimal impact on recyclate quality. The addition of 10% EVOH increased the elastic modulus of PP granulate and cast-PP (cPP) film by 26% and 14%, respectively, and improved oxidation stability by 9%, while reducing cPP film impact strength by 77%. Ormocer^® decreased mechanical performance, particularly elongation at break (-18%), likely due to defect-inducing particles, but had limited influence on MFR. Labels and Ormocer^® also introduced odor variations. Overall, the findings indicate that EVOH up to 10% and labels up to 12.5% yield promising results, providing guidance for designing recyclable, monomaterial packaging.