Decoding Desulfurization Pathways in Metal-Organic Frameworks (MOFs) via Experimental and Computational Approaches: A
Mohd Mehtab1, Mohd Zeeshan1, Manjeet Kumar2
1Functional Inorganic Materials Lab (FIML), Department of Chemistry, Aligarh Muslim University, Aligarh 202002, India.
Abstract:
Two new metal-organic frameworks, {[Cu2(BPDC)2(Bipy)2]·2DMF}n (MM-1) and {[Zn3(BPDC)3(Bipy)]4H2O·2DMF}n (MM-2), were synthesized using biphenyl-4,4'-dicarboxylic acid (BPDC) and 4,4'-bipyridine (Bipy) mixed linkers via a solvothermal route. Single-crystal X-ray diffraction (SCXRD) showed both frameworks adopt an sra topology with robust 3D architectures stabilized by π-π and metal-ligand interactions. FTIR, TGA, BET, PXRD, and XPS analyses confirmed structural integrity and coordination environments. XPS identified Cu2+ centers in MM-1 (Cu 2p3/2: 933.38 eV; Cu 2p1/2: 951.24 eV) and Zn2+ centers in MM-2 (Zn 2p3/2: 1022.97 eV; Zn 2p1/2: 1045.42 eV), while N 1s peaks at 398.5 and 399.8 eV verified coordinated and uncoordinated pyridyl nitrogen. N2 sorption studies at 77 K revealed mesoporosity with surface areas of 597.29 m2 g-1 (MM-1) and 128.97 m2 g-1 (MM-2). MM-1 showed excellent dibenzothiophene (DBT) and benzothiophene (BT) adsorption capacities of 91.82 and 78.80 mg g-1, respectively, achieving ∼87% DBT removal-superior to most reported MOFs. Further, DFT calculations supported strong thermodynamic binding, with mode 4 exhibiting the most favorable adsorption energy due to π-π stacking and O···S interactions. The synergy between open Cu2+ sites, high surface area, and the strong host-guest interactions positions MM-1 as a promising desulfurization material.