Effect of tightening protocols on abutment screw loosening and morphological changes in two-piece zirconia implants:...

This study evaluates the effects of different abutment screw tightening protocols and implant materials on screw loosening and morphological changes after cyclic torsional loading of two-piece implants.

Titanium (T) and zirconia (Z) two-piece implants were used. Abutment screws were tightened to 35 Ncm. Three protocols were tested: (A) retightening after 5 min, (B) immediate retightening, and (C) no retightening (n = 6 each). All samples underwent 100,000 cycles of cyclic torsional loading. Removal torque values before and after loading (RT-pre and RT-post) and torque loss percentage (TL) were calculated. Surface morphology was assessed using scanning electron microscopy (SEM), and dimensional changes were quantified using root mean square (RMS) values from three-dimensional data.

In the titanium group, protocol A (TA) had lower RT-post values than protocols B (TB) and C (TC) (P < 0.001), and TB was lower than TC (P < 0.05). In the zirconia group, protocol A (ZA) was significantly lower than protocols B (ZB) and C (ZC) (P < 0.05, P < 0.001, respectively). RT-post and RT-pre were significantly lower in the zirconia group than in the titanium group under all conditions (P < 0.001). No differences were observed in TL. SEM revealed wear on the screw heads and threads in all groups. RMS values were significantly lower in the zirconia group (P < 0.05).

Abutment screw retightening does not consistently enhance torque maintenance under torsional loading. The implant material affects torque retention and deformation, where titanium implants demonstrating greater stability than zirconia implants.