Photocatalytic NO_x Removal Performance of TiO₂-Coated Permeable Concrete: Laboratory Optimization and Field...

Nitrogen oxides (NO_x) emitted mainly from vehicle exhaust significantly contribute to urban air pollution, leading to photochemical smog and secondary particulate matter. Photocatalytic technology has emerged as a promising solution for continuous NO_x decomposition under ultraviolet (UV) irradiation. This study developed an eco-friendly permeable concrete incorporating activated loess and zeolite to improve roadside air quality. The high porosity and adsorption capability of the concrete provided a suitable substrate for a TiO₂-based photocatalytic coating. A single-component coating system was optimized by introducing colloidal silica to enhance TiO₂ particle dispersibility and adding a binder to secure durable adhesion on the concrete surface. The produced permeable concrete met sidewalk quality standards specified in SPS-F-KSPIC-001-2006. Photocatalytic NO_x removal performance evaluated by ISO 22197-1 showed a maximum removal efficiency of 77.5%. Even after 300 h of accelerated weathering, the activity loss remained within 13.8%, retaining approximately 80% of the initial performance. Additionally, outdoor mock-up testing under natural light confirmed NO_x concentration removal and formation of nitrate by-products, demonstrating practical applicability in real environments. Overall, the integration of permeable concrete and a durable, single-component TiO₂ photocatalytic coating provides a promising approach to simultaneously enhance pavement sustainability and reduce urban NO_x pollution.