New Technology for the Production of Transparent Glass Coatings from Multi-Alloy Targets with Antibacterial Activity

Antibacterial thin-film coatings are of increasing interest for enhancing hygiene in controlled environments such as commercial greenhouses. Phytopathogens including Pseudomonas syringae, and human pathogens such as Escherichia coli, Micrococcus luteus, and Staphylococcus aureus, frequently contaminate greenhouse environments. The present study aimed to develop and evaluate multifunctional magnetron-sputtered glass coatings with strong antimicrobial performance, deposited by physical vapor deposition to achieve precise control of film composition and uniform coverage of large substrates (≥0.25 m²), ensuring industrial-scale applicability. Thin films were fabricated by magnetron sputtering using multi-alloy targets composed of Cu, Sn, Zn, Al, Ni, Fe, Ti, Mn, Nb, or Co. Fourteen distinct coating compositions were characterized using high-resolution transmission electron microscopy, scanning transmission electron microscopy, and energy-dispersive X-ray spectroscopy. Antibacterial performance was evaluated against the following strains: E. coli (PCM 2560), M. luteus (PCM 525), S. aureus (PCM 2602), and P. syringae pv. tomato (IOR2146). Coatings prepared from 90%Cu-10%Sn, 90%Cu-10%Zn, and 80%Cu-20%Ti targets exhibited one of the highest antibacterial efficiencies. These coatings also showed strong mechanical durability and corrosion resistance. Our results indicate that coatings obtained from Cu-based multi-alloy targets by magnetron sputtering are promising candidates for use as durable, antimicrobial inner glass surfaces in future greenhouse applications.