Characteristics of Particleboards Made from Esterified Rattan Skin Particles with Glycerol-Citric Acid: Physical,...

This study evaluated the effects of glycerol-citric acid (Gly-CA) modification and polyurethane (PU) adhesive concentration on the properties and termite resistance of rattan skin-based particleboards. Rattan skin particles were modified with 0%, 20%, and 40% Gly-CA and bonded using 6% or 12% PU adhesive. Gly-CA modification significantly improved dimensional stability, reducing water absorption and thickness swelling to about 35-40% and 4-6%, respectively, at 40% Gly-CA with 12% PU. However, excessive modification decreased mechanical strength due to over-crosslinking, while 20% Gly-CA provided the best balance between strength and stability. FTIR analysis confirmed ester and urethane bond formation, while thermogravimetric results showed enhanced thermal stability with increasing Gly-CA content (T_max up to 356.8 °C). Field tests conducted over 98 days revealed a substantial improvement in durability, with termite-induced mass loss decreasing from about 28% in untreated boards to below 8% in Gly-CA-modified samples. From this study, the combination of 40% Gly-CA modification and 12% PU adhesive produced particleboards with improved dimensional and thermal stability, as well as durability against termites. These findings highlight glycerol-citric acid bio-modification as a sustainable and effective strategy for developing durable eco-friendly rattan skin-based composites.