Sustainable High Corrosion Resistance in High-Concentration NaCl Solutions for Refractory High-Entropy Alloys with...

Among corrosive environments, Cl^- is one of the most aggressive anions which can cause electrochemical corrosion and the resultant failures of alloys, and the increase in Cl^- concentration will further deteriorate the passive film in many conventional alloys. Here, we report single-phase Nb₂₅Mo₂₅Ta₂₅Ti₂₀W₅C_x (x = 0.1, 0.3, 0.8 at.%) refractory high-entropy alloys (RHEAs) with excellent corrosion resistance in high-concentration NaCl solutions. According to potentiodynamic polarization, electrochemical impedance spectroscopy, corroded morphology and the current-time results, the RHEAs demonstrate even better corrosion resistance with the increase in NaCl concentration to 23.5 wt.%, significantly superior to 304 L stainless steel. Typically, the corrosion current density (i_corr) and over-passivation potential (E_t) reached the lowest and highest value, respectively, in the 23.5 wt.% NaCl solution, and the i_corr (2.36 × 10^-7 A/cm²) of Nb₂₅Mo₂₅Ta₂₅Ti₂₀W₅C_0.1 alloy is nearly two orders lower than that of 304 L stainless steel (1.75 × 10^-5 A/cm²). The excellent corrosion resistance results from the formation of passive films with fewer defects and more stable oxides. Moreover, with the addition of the appropriate C element, the RHEAs also demonstrated improved strength and plasticity simultaneously, for example, the Nb₂₅Mo₂₅Ta₂₅Ti₂₀W₅C_0.3 alloy exhibited an average yield strength of 1368 MPa and a plastic strain of 19.7%. The present findings provide useful guidance to address the conflict between the excellent corrosion resistance and high strength of advanced alloys.