Comparative Analysis of Annealing-Dissolution Techniques for Hollow Submicron Metal Oxide Fiber Synthesis

Double-shell ZnO/Al₂O₃ submicron hollow fibers were successfully fabricated through a combined electrospinning and atomic layer deposition (ALD) approach. Polyvinyl alcohol (PVA) fibers were first produced by electrospinning and subsequently coated with a conformal Al₂O₃ barrier layer via low-temperature ALD employing trimethylaluminum (TMA) and deionized (DI) H₂O to preserve the integrity of the temperature-sensitive polymer core. The inner polymer was then removed using two different techniques-thermal annealing and water dissolution-to compare their effects on the fiber morphology. Finally, a functional ZnO layer was deposited by thermal ALD with diethylzinc (DEZ) and DI H₂O. It was found that the polymer removal method critically determined the final structural and morphological characteristics of the fibers. Thermal annealing resulted in smooth, shrunken fibers, while water dissolution led to diameter expansion and the formation of a highly rough, bubble-like surface structure due to swelling-induced micro-cracking. The selection of the polymer removal method offers a precise and controllable route for tailoring the fiber morphology. The resulting high-aspect-ratio (HAR) structures, particularly the rough and expanded fibers, exhibit enhanced specific surface area, making them highly promising for applications in sensing, catalysis, and filtration.