Composition-Driven Ultra-Low Hysteresis Electrostrictive Strain in BaTiO₃-BaZrO₃-Bi(Zn_2/3Nb_1/3)O₃ Ceramics with High...

High electrostrain, excellent thermal stability, and low hysteresis are critical requirements for advanced high-precision actuators. However, simultaneously achieving these synergistic properties in lead-free ferroelectric ceramics remains a significant challenge. In this work, a targeted B-site doping strategy was employed to develop novel lead-free (0.99-x)BaTiO₃-xBaZrO₃-0.01Bi(Zn_2/3Nb_1/3)O₃ (BT-xBZ-BZN, x = 0-0.2) ceramics. Systematic investigation identified optimal Zr⁴⁺ substitution at x = 0.1, which yielded an outstanding combination of electromechanical properties. For this optimal composition, a high unipolar electrostrain (S_max = 0.11%) was achieved at 50 kV/cm, accompanied by an ultra-low hysteresis (H_S = 1.9%). Concurrently, a large electrostrictive coefficient (Q₃₃ = 0.0405 m⁴/C²) was determined, demonstrating excellent thermal robustness with less than 10% variation across a broad temperature range of 30-120 °C. This superior comprehensive performance is attributed to a composition-driven evolution from a long-range ferroelectric to a pseudocubic relaxor state. In this state, the dominant electrostrictive effect, propelled by reversible dynamics of polar nanoregions (PNRs), minimizes irreversible domain switching. These findings not only present BT-xBZ-BZN (x = 0.1) as a highly promising lead-free candidate for high-precision, low-loss actuator devices, but also provide a viable design strategy for developing high-performance electrostrictive materials with synergistic large strain and superior thermal stability.