Durable and Robust Janus Membranes with Asymmetric Wettability Based on Poly (Vinylidene Fluoride)/Polyvinyl Alcohol...

With the acceleration of industrialization, the problems of water resource pollution and shortage caused by oil spills and industrial wastewater discharge have become increasingly severe, posing a major threat to ecological sustainable development. Therefore, efficient oil-water separation technology has become a key breakthrough to alleviate this crisis. In this study, Janus membranes with asymmetric wettability were prepared by layer-by-layer electrospinning. The influence of the thickness ratio between the hydrophobic layer and the hydrophilic layer on the mechanical properties, separation flux, and oil-water mixture efficiency of the Janus membranes was examined, and an optimized membrane configuration was determined: the optimal thickness ratio between hydrophobic and hydrophilic layers was 4:6. Under these conditions, the fracture stress of the fiber membranes reached 99% MPa, the fracture strain was 55.63 ± 4.77%, the separation flux values were 1888.22 and 1042.66 L m^-2 h^-1 for the oil-water mixture and water-in-oil emulsion, respectively, with the separation efficiencies all exceeding 99%. After 50 cycles of separation for two different oil-in-water emulsions, the separation flux and separation efficiency of the optimal sample remained relatively stable, demonstrating strong practicability. In general, the Janus fiber membranes met the expected requirements, laying a good foundation for future applications in oil-water separation, floating oil collection in water, and other fields.