Swelling Property and Metal Adsorption of Dialdehyde Crosslinked Poly Aspartate/Alginate Gel Beads

Dialdehyde crosslinked poly aspartate/alginate hydrogel beads were synthesized by covalently introducing poly aspartate into the alginate network via dialdehyde-mediated crosslinking, and the resulting effects on swelling and adsorption behavior were investigated. Alginate was partially oxidized to form dialdehyde alginate and crosslinked with poly aspartic acid via Schiff base formation, followed by ionic crosslinking with calcium ions. The chemical structure and morphology of the gel beads were characterized by Fourier transform infrared spectroscopy and scanning electron microscopy. Incorporation of PAsp significantly altered the swelling behavior of alginate-based gel beads. In saline solution, PAsp-modified gel beads exhibited a swelling ratio of approximately 112 g/g, which was higher than that of calcium alginate gel beads. This behavior is suggested to be associated with changes in the alginate-calcium network structure induced by polymer modification. PAsp-modified gel beads exhibited moderate but distinct adsorption behavior depending on the adsorbate. Removal efficiencies of approximately 40-50% were observed for copper and cobalt ions, while a removal efficiency of around 50% was obtained for the cationic dye crystal violet. In contrast, adsorption of the anionic dye Congo red decreased with increasing PAsp content, indicating charge-dependent adsorption behavior. Overall, this study demonstrates that PAsp modification via dialdehyde-mediated crosslinking influences both the swelling and adsorption properties of alginate-based hydrogel beads. The results provide fundamental insight into how network modification can be used to tune the behavior of alginate-based hydrogels in aqueous environments.