Surface Activation Using Atmospheric Plasma to Improve PHB Coating Adhesion and Corrosion Resistance of AZ91D...

Polyhydroxybutyrate (PHB) is considered a coating material capable of limiting the corrosion of biodegradable metallic implants due to its biocompatibility and ability to form a physical barrier. In this study, PHB was deposited on commercial AZ91D magnesium alloy using the spin coating technique. To improve adhesion at the polymer-substrate interface, the magnesium substrates were subjected to atmospheric pressure plasma treatment for different exposure times (5, 10, or 15 min) before coating. The optimal treatment time of 5 min significantly increased substrate wettability and surface free energy, facilitating stronger PHB adhesion. In addition, the PHB coatings were subjected to atmospheric pressure plasma treatment for 5, 10, or 15 s to evaluate potential surface modifications. Corrosion behavior under simulated physiological conditions was assessed via potentiodynamic polarization and electrochemical impedance spectroscopy (EIS) in HANK's solution at 37 °C. Pull-off tests were used to evaluate the adhesion strength between the coating and the substrate under each treatment condition. The results showed a significant decrease in the corrosion rate (V_corr), from 4.083 mm/year for bare Mg-AZ91D to 0.001 mm/year when both the substrate and the polymer received plasma treatment. This indicates that the treatment modifies surfaces and improves interfacial bonding, enhancing polymer-metal interaction and producing durable, biocompatible coatings for medical implants.