Tribological Performance of Grease-Coated Rubber in High-Pressure Hydrogen Storage Applications

Rubber materials undergo continuous wear in high-pressure seal applications. To address the risk of adhesive wear and consequent leakage of rubber seals operating under reciprocating sliding in high-pressure hydrogen storage and refueling systems, this study employed high-pressure hydrogen tribology testing. Ball-on-disk reciprocating tests were conducted using a 316L stainless-steel ball against silica-filled nitrile butadiene rubber (NBR), and the friction response and wear-morphology evolution were compared under ambient air, 1 MPa hydrogen (H₂), 50 MPa H₂, 50 MPa nitrogen (N₂), and grease-coated conditions. Under dry sliding, the coefficient of friction (COF) of NBR in air and hydrogen ranged from 1.34 to 1.44, whereas it decreased markedly to 0.942 in 50 MPa N₂. The wear volume under the four dry conditions was concentrated in the range of ~0.292-0.320 mm³. After grease coating, the steady-state COF in air and at 50 MPa H₂ dropped to 0.099 and 0.105, respectively, and the wear features changed from ridge-like wear patterns/tear pits to regular, smooth indentations with slight running marks. The results demonstrate that a lubricating film can effectively separate direct metal-rubber contact and suppress stick-slip, enabling a low-friction, low-wear, and highly stable interface in high-pressure hydrogen, and providing a practical engineering route for reliable operation of rubber seals in hydrogen service.