Ultrasonic-Assisted Extrusion Processing for Enhancing Physical Properties of High-Density Polyethylene by...

The evolution of crystallinity resulting from stress imposed on a melt, known as flow-induced crystallinity, can strongly influence the mechanical and physical properties of semicrystalline polymers. This study investigates shear-induced crystallization by applying an ultrasonic field to the melt flow as it passes through dies with various geometries. A custom-built sonication die is employed for controlling the dynamic temperature and shear environment, resulting in molecular alignment and potential for flow-induced crystallization. Application of both conventional and ultrasonic shear rates at the equilibrium melt temperature of high-density polyethylene (HDPE) was investigated to accelerate crystallinity and manipulate the crystal morphology across the film in pursuit of improved mechanical and gas barrier properties without the need for additives or other polymer layers. The relationships among ultrasonic-assisted extrusion processing, polymer structure, and performance were analyzed using wide- and small-angle X-ray scattering (WAXS and SAXS), tensile testing, and oxygen transmission rate (OTR) analysis. Multiple linear regression models were implemented to predict the correlation among HDPE structure, process, and properties. Structural analysis revealed that both conventional and ultrasonic shear rates had the most significant influence on lamellar spacing and redistribution of rigid and soft amorphous fractions within the crystalline domains, ultimately dictating the mechanical and physical properties of the films. The goal is to explore the potential of the ultrasonic-assisted high crystallinity monolayer that can replace some of the functionality of complex, heterogeneous multilayer packaging with a single-material film having enhanced oxygen barrier properties.