Unveiling the Degradation Mechanism of Impermeability and Pore Structure in Concrete Under Long-Term Water Exposure

To investigate the evolution of impermeability and pore structure in concrete under long-term service, systematic tests were conducted on submerged concrete from dam sections with over 75 years of service. Results show that the surface water permeation resistance index of concrete in the downstream section of the main dam is only 9.19 × 10^-9, significantly lower than that of concrete from the upstream of the main dam (UMD), downstream of the main dam (DMD), upstream of the auxiliary dam (UAD), and upstream of the weir (UW). Moreover, its impermeability improves noticeably within the 0-100 mm depth range. Mercury intrusion porosimetry revealed that the median pore diameter, average pore diameter, pore content, and porosity in this region reach 306.7 nm, 55.4 nm, 35.64%, and 3.961 mm, respectively-all markedly higher than in other dam sections. Combined XRD and SEM/EDS analyses indicate that crystallization pressure from saline solutions in the coastal environment, together with long-term carbonation, leads to structural loosening and increased porosity in the downstream concrete of the main dam, ultimately degrading its impermeability performance.