Small punch testing and scanning electron microscopy analysis of damage evolution in dual-phase steel

Asim Alsharif1, Syed Quadir Moinuddin2, Christophe Pinna3

  • 1Department of Mechanical Engineering, College of Engineering in Yanbu, Taibah University, Yanbu Al-Bahr, 46425, Saudi Arabia. aasharif@taibahu.edu.sa.

Scientific Reports
|February 16, 2026
PubMed
Abstract

No abstract available in PubMed .

Keywords:
Crack initiation and propagationDigital image correlationDual phase (DP 1000) steelMicrostructure damage and modellingSP test (biaxial loading)Scanning electron microscope

More Related Videos

Co-localizing Kelvin Probe Force Microscopy with Other Microscopies and Spectroscopies: Selected Applications in Corrosion Characterization of Alloys12:18

Co-localizing Kelvin Probe Force Microscopy with Other Microscopies and Spectroscopies: Selected Applications in Corrosion Characterization of Alloys

Published on: June 27, 2022

3.4K
Micromechanical Tension Testing of Additively Manufactured 17-4 PH Stainless Steel Specimens05:38

Micromechanical Tension Testing of Additively Manufactured 17-4 PH Stainless Steel Specimens

Published on: April 7, 2021

3.9K

Related Concept Videos

Mechanical Characteristics of Steel01:18

Mechanical Characteristics of Steel

The mechanical characteristics of steel are assessed through various tests that evaluate its strength, toughness, and flexibility. These tests include tension, torsion, impact, bending, and hardness assessments, each providing crucial information about steel's suitability for specific applications.
The tension test is fundamental for determining tensile strength. In this test, a steel specimen is stretched using a gripping device until it breaks. The data collected during this test are used...
1.1K
Microcracking in Concrete01:20

Microcracking in Concrete

Microcracking in concrete refers to the tiny cracks that can form within the material even before any external load is applied. These microcracks typically occur at the interface between the coarse aggregate and the hydrated cement paste, often as a result of differential volume changes prompted by variations in stress-strain behavior, as well as thermal and moisture movement. Initially, these microcracks remain stable and do not grow substantially until the concrete is stressed to about 30...
500