Supramolecular Effects of Alkyl Sulfonates in Silver Nanocrystal Synthesis

While cationic surfactants such as hexadecyltrimethylammonium bromide (CTAB) are ubiquitous in the synthesis of noble metal nanocrystals, anionic surfactants are rarely used. This work explores the addition of sodium alkyl sulfonates with chain lengths ranging from one to eight carbons to a silver nanoplatelet reaction. Short-chain sulfonates comprised of one to four carbons show little effect on the nanocrystal synthesis, but alkyl sulfonates comprised of five or more carbons at concentrations above 1 mM have a pronounced effect on the absorbance of the nanocrystals, causing a blue-shift in the wavelength of maximum absorbance (λ_max) from approximately 800 to 400 nm as the sulfonate concentration is increased to 7 mM. Higher concentrations of sulfonate result in a subsequent red-shift of the peak. Investigation into the possible formation mechanisms responsible for this synthetic control revealed the absence of sulfonate micelles under the reaction conditions. Instead, we hypothesize that sulfonate bilayers are nucleated around the silver nanocrystals at concentrations below the critical micelle concentration and interact with either the citrate ligands or the silver surface to influence nanocrystal morphology, and thus absorbance. Strikingly, the addition of long-chain alkyl sulfonates to already-synthesized nanocrystals results in similar changes to the nanocrystal absorbance that occur within seconds, providing further support for the proposal that these effects are related to the surface chemistry of the nanocrystals, which appear to be highly dynamic.