Mechanism of High-Temperature Thickening Regulation in Amide-Modified Ultra-High-Temperature Polycarboxylate...

As oil and gas well development moves towards ultra deep formations, the high temperature at the bottom of the well causes the failure of copolymer retarders, leading to increased risk of oil and gas leakage and carbon emissions during cementing operations. To further ensure the safety of high-temperature oil and gas cementing operations, the influence of N,N-dimethylacrylamide (DMAA) on the high-temperature performance of copolymer retarders was explored. DMAA was introduced into copolymer retarders to form ultra-high temperature retarders. By analyzing the micro mechanism of copolymer retarders, the regulation of high-temperature retarders on the micro hydration process of cement slurry at high temperatures was revealed. Results showed that the cement slurry containing 3.0% SH5L (Pentameric copolymer retarder-introduced DMAA) exhibits a significantly similar thickening time with 3.4% SH4L (Quaternary copolymer-retarder) at 180 °C, demonstrating superior retardation performance at a lower dosage. The ultra-high-temperature polycarboxylate retarder SH5L was prepared by introducing the DMAA, enhancing its temperature resistance and retardation performance at high temperatures. The coupling of SH5L and Ca²⁺ retards the hydration and crystallization process of the cement slurry. The combination of rigid polycyclic structures and cationic monomers weakens the chelation between anionic groups and Ca²⁺, inhibiting the curling of polymers in ionic solutions. Polymer chains stretch with increasing temperature, enhancing their ability to bind with Ca²⁺ and improving their high-temperature retardation performance.