Synthesis and Structure-Property Relationships of PLLA-Based ABA Triblock Copolymers with Bio-Based Soft Segments

The development of biodegradable ABA-type triblock copolymers with tailored thermo-mechanical performance requires precise control over polymer architecture and phase behavior. In this study, PLLA-based ABA triblock copolymers were synthesized using two structurally distinct, fully bio-based soft segments: poly(methyl ricinoleate) (PMR) and poly(1,3-propanediol) (PPD). To the best of our knowledge, this is the first report on PLLA triblock copolymers incorporating PMR as a renewable soft middle block. Hydroxyl-terminated PMR and PPD were employed as macroinitiators for the controlled ring-opening polymerization of L-lactide, enabling systematic variation in block composition and molecular weight. Structural characterization confirmed successful block formation, while thermal and mechanical analyses revealed pronounced differences in phase separation and structure-property relationships. Copolymers containing PMR exhibited enhanced phase separation, increased crystallinity of PLLA domains, and significantly improved elongation at break, attributed to the presence of pendant chains in the soft segment. In contrast, PPD-based copolymers showed reduced phase separation and more PLA-like mechanical behavior. These results demonstrate that the chemical architecture of bio-based soft segments plays a decisive role in governing the thermo-mechanical performance of PLLA-based triblock copolymers.