Effect of HfC Addition on Microstructure and Wear Resistance of CoCrFeNiTi Coatings Fabricated by Laser Cladding

HfC possesses high hardness, high melting point, and excellent thermal stability, and is regarded as an important wear-resistant reinforcing phase material. In this study, the laser cladding technique was employed to fabricate CoCrFeNiTi and CoCrFeNiTi/HfC composite coatings on the surface of Q235 substrate. The influence of HfC addition on the phase structure evolution, microstructure, and wear resistance of the coatings was systematically investigated. The results showed that the addition of HfC did not alter the phase structure of the coating, which remained dominated by an FCC solid solution. However, they induced the formation of an in situ TiC strengthening phase and reduced the brittle Laves phase content, thereby optimizing the coating's toughness. At the same time, the coating transformed from columnar to equiaxed crystals, with significantly finer grains and further improved structural uniformity. Compared with the CoCrFeNiTi coating, the CoCrFeNiTi/HfC composite coating exhibited a more stable friction coefficient, a significantly lower wear rate, and improved wear resistance by approximately 2.4 times. The performance improvement was mainly attributed to the load-bearing strengthening and crack-pinning effect of the in situ TiC, the inhibitory effect of the reduction in the Laves brittle phase on adhesive wear, and the synergistic effect of Hf, which forms a stable oxidation-protective film during friction.