Structure-Property Relationships in Cyanate Ester Composites Incorporating BaTiO₃ and Transparent Glass Fillers

Polymer-ceramic composites based on cyanate ester resins have attracted increasing attention for high-frequency electronic applications due to their low dielectric loss, thermal stability, and dimensional reliability; however, achieving a targeted dielectric constant while maintaining low loss remains a key challenge. In this study, transparent glass powders and BaTiO₃ ceramic fillers were incorporated into a cyanate ester matrix to systematically investigate structure-property relationships and optimize dielectric performance for antenna-related applications. Transparent glass powders were synthesized via a melt-quenching route and combined with submicron BaTiO₃ particles, while both fillers were surface-modified using 3-triethoxysilylpropyl isocyanate (TESPI) to enhance interfacial compatibility. Composite samples containing 5-30 wt% total filler were fabricated and characterized by XRD, FTIR, tensile testing, dielectric measurements, and SEM/EDX analyses. The results demonstrate that TESPI surface modification promotes strong interfacial bonding and homogeneous filler dispersion within the cyanate ester matrix. An optimal balance between mechanical integrity and dielectric performance was achieved at 15 wt% total filler loading (K3), exhibiting a dielectric constant close to 10 and the lowest dielectric loss (tan δ ≈ 0.0047 at 1 MHz). Microstructural observations confirm that excessive filler loading leads to agglomeration and increased dielectric loss. Overall, the combined use of transparent glass and BaTiO₃ fillers, together with effective interfacial engineering, enables precise tuning of dielectric properties in cyanate ester composites for high-frequency electronic applications.