Biodegradable Poly(lactic acid)-Based Blends as Intrinsic Self-Healing Matrices for Multifunctional and...

In this work, compatibilized poly(lactic acid)/poly(butylene adipate-co-terephthalate) (PLA/PBAT) blends were developed and characterized, to be potentially utilized as biodegradable self-healing matrices for composite laminates. Blends containing 10, 20 and 30%wt of PBAT and 0.5 phr of an epoxy-based compatibilizer were prepared by melt compounding and hot pressing. Rheological measurements showed that moduli and complex viscosity generally increased with PBAT content, while maintaining viscosity levels suitable for conventional melt-processing operations. FT-IR and FESEM analyses confirmed the formation of an immiscible but well-compatibilized morphology, characterized by a homogeneous dispersion of PBAT domains within the PLA phase. Mechanical tests revealed a decrease in tensile modulus (up to 44%), strength (up to 45%) and fracture toughness (up to 40%) with a PBAT content up to 30%wt. Self-healing was evaluated by measuring the fracture toughness (K_IC) recovery after thermal treatment at 140 °C. After healing, the blend containing 20%wt of PBAT exhibited a self-healing efficiency of 64% under impact conditions, which was attributed to the smoother fracture surface generated at an elevated strain rate that facilitated a more effective flow of the molten PBAT phase across the crack interface during healing. The formulation containing 20%wt of PBAT featured the best balance between mechanical performance and self-healing efficiency.