Composition-Controlled Photocatalytic and Antibacterial Performance of ZnO-ZnS Nanocomposite Catalysts Synthesized by...

Zinc oxide (ZnO) and zinc sulfide (ZnS) nanocomposites represent promising multifunctional photocatalysts due to their complementary band structures and synergistic charge separation. ZnO-ZnS nanocomposites with varied ZnS content were synthesized to elucidate the composition-structure-property relationships governing their multifunctional performance. Structural characterization using XRD, SEM/EDS, Raman spectroscopy, and XPS confirmed the coexistence of wurtzite crystalline phases of ZnO and ZnS. SEM analysis revealed ZnS fine deposition on the ZnO surface. XPS measurements showed a gradual increase in the amount of ZnS on the ZnO surface with increasing sulfide content and a shift in the valence band maximum from 2.32 eV (pure ZnO) to 0.77 eV (pure ZnS). Optical measurements (IR, UV-Vis diffuse reflectance, photoluminescence) demonstrated that, despite the evolution of vibrational and luminescence features characteristic of ZnS, the apparent band gap remained nearly constant at 3.16-3.18 eV across the series. Photocatalytic methylene blue (MB) degradation followed pseudo-first-order kinetics, peaking for ZN_2 (1% ZnS, k_app = 103 × 10^-3 min^-1), which is 1.7 times higher than for pure ZnO. This enhanced performance is consistent with an S-scheme-like heterojunction that facilitates electron migration to the ZnS conduction band while retaining ZnO valence band holes for oxidation. Scavenging experiments confirmed that electrons dominate MB degradation (k_app up to 185.1 × 10^-3 min^-1 with EDTA/t-BuOH/Ar), outperforming hole-mediated pathways. Antibacterial assays against Staphylococcus aureus revealed good antimicrobial activity for all nanoparticles. The nanocomposite's antibacterial activity was similar across all samples and was only slightly lower than that of pure ZnS and ZnO.