Multi-Scale Tribo-Thermo-Viscoelastic Engineering of Sustainable Bio-Based Epoxy Through Hybrid Carbon Nano...

This study investigates the multi-scale tribo-thermo-viscoelastic performance of a sustainable bio-based FormuLITE epoxy reinforced with single and hybrid carbon nanofillers (0.1 wt.% total loading) under dry sliding up to 50 N. Pin-on-disk tests at 10, 30, and 50 N showed a consistent reduction in contact pressure and wear volume in the order: neat epoxy > 0.1 CNT > 0.1 GNP > 0.1 ND > 0.1 CNT/GNP > 0.1 CNT/ND > 0.1 GNP/ND. At 50 N and 1500 m sliding distance, neat epoxy exhibited a wear volume of 13.43 mm³ and contact pressure of 13.4 N/cm², while the GNP/ND hybrid reduced wear to 4.86 mm³ and contact pressure to 6.2 N/cm², corresponding to reductions of 64% and 54%, respectively. The accelerating wear coefficient decreased from 2.9 × 10^-6 to 8.5 × 10^-7, confirming slower damage accumulation in hybrid systems. Time-dependent contact pressure analysis revealed reduced asymptotic intensity and suppressed mid-cycle pressure spikes, indicating enhanced tribolayer stability. Effective surface hardness increased from 0.18 GPa (neat epoxy) to 0.30 GPa (GNP/ND), while normalized wear decreased from 1.00 to 0.36. Enhanced damping behavior and improved thermal conductivity in hybrid systems promoted stress redistribution and minimized flash-temperature localization. An interfacial energy-partition framework calibrated to experimental wear data quantitatively linked effective driving pressure, tribofilm stabilization, and surface hardness to material removal. The results demonstrate that wear mitigation in sustainable bio-epoxy systems is governed by coupled mechanical, viscoelastic, and thermal energy redistribution, with GNP/ND hybrids providing the most stable tribological interface under severe sliding. The findings contribute to the development of durable and sustainable bio-epoxy composite systems for engineering applications, supporting broader goals of responsible material utilization and sustainable industrial innovation aligned with the United Nations Sustainable Development Goals (SDG 9 and SDG 12).