Experimental Study on the Influence of Ultraviolet Aging on the Shear Characteristics of HDPE Geomembrane/Sand...

High-density polyethylene (HDPE) geomembranes (GMs) in landfill liners experience UV exposure during installation. While tensile strength deterioration after UV aging is known, changes in interfacial shear properties are rarely reported. This study investigates the evolution of interfacial shear behavior at the GM/sand interface by subjecting GM specimens to varying durations of indoor UV aging followed by direct shear tests. Underlying mechanisms were explored through tensile strength, melt flow index, crystallinity, and oxidation induction time (OIT) measurements. Results show that displacement required to reach peak shear strength for smooth geomembrane (GMS)/sand interface decreased with aging time (49.0-70.1% reduction), while no clear trend emerged for textured geomembrane (GMX)/sand interface. Following 80 days of UV exposure, the GMS/sand interfacial shear strength declined, with the peak friction angle dropping 20.6% from 26.2° to 20.8°. For the GMX/sand interface, the peak friction angle dropped to its lowest value of 31.2° after 40 days of exposure (from 34.3°), and then exhibited an increase with further UV aging. The large displacement shear strength followed a trend similar to that of the peak strength. Among the other tested indicators, the variation pattern of OIT with UV exposure exhibited the best correlation with the GMS/sand interface shear strength.