Industrial-Scale Copper Wear Reduction in the Electrical Discharge Machining Through Hydrostatic Extrusion

The study focused on the development and optimization of plastic deformation of pure M1E copper using an unconventional hydrostatic extrusion (HE) process aimed at improving the performance of electrodes used in electrical discharge machining (EDM). The process was designed to refine the microstructure while maintaining the high electrical conductivity required for EDM applications. Optimization of a three-stage HE process (cumulative strain ε = 2.51) resulted in the formation of an ultrafine-grained structure (d₂ ≈ 370 nm), leading to a significant increase in mechanical strength (UTS ≈ 400 MPa) while preserving very high electrical conductivity (~99% IACS). This combination of properties is particularly important for EDM electrodes, as it allows improved wear resistance without compromising electrical performance. Due to the application-oriented nature of the study, the HE-processed copper was tested under industrial EDM conditions. Wear tests were conducted using seven electrodes of different geometries required for the production of a sample injection mold. The results demonstrated a substantial reduction in electroerosion wear of HE-processed electrodes (30-90%) compared with undeformed copper, together with up to 25% improvement in surface quality. These findings indicate that hydrostatic extrusion is an effective method for producing high performance EDM electrode materials with improved durability and machining quality.