Tri-Magnesium Phosphate as a Candidate Biocompatible Retarder for Magnesium Potassium Phosphate Cement: Setting...

Magnesium potassium phosphate cement (MKPC) is a promising bone repair material but suffers from excessively rapid setting time (typically within minutes) that limits clinical application. This study systematically investigates trimagnesium phosphate (TMP) as a candidate retarding additive for MKPC. TMP was used to partially replace dead-burned magnesium oxide at replacement levels of 0%, 10%, and 15% by mass. The effects of TMP content, water-to-cement ratio (0.17-0.23), and magnesium-to-phosphate molar ratio (4-10) on setting time, fluidity, hydration kinetics, compressive strength, and microstructure were comprehensively evaluated. Results show that TMP effectively extends the setting time from 9-13 min (without TMP) to 10-19 min, providing a working window that may be suitable for biomedical applications requiring extended handling time. Notably, 10% TMP incorporation enhances early compressive strength, with 1-day strength reaching 35.2 MPa compared to 28.5 MPa for control samples. Hydration heat analysis reveals TMP moderates the acid-base reaction kinetics through its slower dissolution rate compared to MgO. Microstructural characterization shows TMP promotes the formation of denser K-struvite crystals with refined microstructure. The optimal TMP dosage of 10% achieves a balanced performance, extending setting time while improving early strength and microstructural densification. These findings establish TMP as an effective retarder for developing MKPC-based materials with potential for biomedical applications, pending further biological validation.