Optimizing the Utilization Rate and Performance of 3D-Printed Mortar with Dual-Size Recycled Sand

To enhance the utilization rate and mechanical performance of recycled sand (RS) in extrusion-based 3D printing, this study investigates the influence of varying incorporation ratios of RS across two particle size fractions: 0.075-1.18 mm (RS01) and 1.18-2.36 mm (RS12). The RS utilization rate was determined via the material balance method, while microstructural mechanisms were analyzed using scanning electron microscopy and Vickers microhardness testing. The results indicate that: a combination of 75% RS01 and 25% RS12 achieves the maximum RS utilization rate of 84.3%. At an RS12/RS01 ratio of 1:3, the printed specimens exhibit the smallest tilt angles in bidirectional buildability tests, measuring 7.6° and 7.2°, with corresponding tan θ values of 0.066 and 0.063. Compared to mortar with 100% RS01, this optimized mixture yields average increases of 36.5% in compressive strength, 40.7% in flexural strength, and 6.8% in interlayer splitting strength. Analysis of variance indicates that different particle size combinations have a significant effect on the mechanical properties. Microhardness analysis reveals that the combination of 75% RS01 and 25% RS12 achieves a minimum interfacial transition zone width of 46 µm. Utilizing larger-particle-size RS in 3D printing effectively enhances its utilization rate while maintaining satisfactory printability and mechanical properties.