Process-Structure Relationships Governing Dimensional Accuracy in Material-Extrusion-Printed PLA-Based Composites

Material extrusion (MEX) additive manufacturing can produce material-dependent variations in dimensional fidelity, internal structure, and deposition stability, even under identical processing conditions. In this study, a comprehensive experimental investigation is conducted on MEX-printed specimens manufactured from a broad set of PLA-based composite materials to quantify these variations and assess their mutual interdependence. Dimensional behavior, internal structural characteristics, and process behavior were systematically investigated using complementary geometric, physical, and deposition-related descriptors. All properties were determined from replicated specimens to ensure statistical robustness, and the resulting datasets were examined using both conventional metrics and multivariate 3D correlation approaches. Compact PLA-based formulations exhibit consistent internal packing, characterized by relative density (RD) values of approximately 0.40-0.46, porosity (ϕ) levels around 55-60%, reduced (≤0.15%) density variability (CV), and small (-0.4-0.0%) volumetric deviations (ΔV). These features reflect stable extrusion and predictable dimensional response. In contrast, foamed, fiber-reinforced, and organic-filled composites display reduced internal packing (RD < 0.40), increased ϕ (>60%), elevated CV (0.27-0.58%), and systematically larger positive ΔV (up to +1.4%), indicating a higher sensitivity to process-induced heterogeneity. Multivariate correlations further reveal that volumetric dimensional distortion is jointly governed by internal packing efficiency and extrusion stability. Overall, the results demonstrate that dimensional accuracy in MEX of PLA-based composites arises from coupled structure-process interactions rather than isolated material or process parameters. The experimental framework proposed here provides quantitative guidance for material selection and process optimization aimed at enhancing geometric fidelity in composite filament fabrication.