Setting Characteristics, Solubility, Bioactivity and Interaction with Dentin of Four Calcium Silicate-Based...

The aim of this study was to evaluate setting time, hardness, solubility, bioactivity and interaction with dentin of four calcium silicate-based sealers (CSBS). Three single-phase CSBS (AH Plus Bioceramic/AHB, CeraSeal/CSL, TotalFill BC/TFL), one powder/liquid CSBS (BioRoot RCS/BRT) and an epoxy control (AH Plus Jet/AHP) were investigated. Setting time was evaluated on glass (G1) and dentin (G2) surfaces, by adding 1%wt purified water to single-phase products. For hardness measurements, the Shore-D hardness test was used. Solubility was assessed according to the ISO 6876:2012 standard. For bioactivity screening, 1-week set specimens were immersed in SBF or water (30 days/37 °C) and examined by ATR-FTIR spectroscopy. Interaction with dentin was tested by ATR-FTIR before and after contact with the sealers. For setting time in G1, all CSBS failed to comply with the ISO standard, while in G2, most materials were set in the range of 6-8 h, except for CSL. The ranking of significant differences in hardness was AHP, BRT > CSL, AHB, TFL. Regarding solubility, AHB, BRT and AHP were found to comply with the ISO standard, whereas CSL and TFL failed. For bioactivity, characteristic peaks of calcium phosphates were found in all CSBS, with TFL being the most bioactive. A chemical interaction between CSBS and dentin was registered, with a strong reduction in collagen peaks and an increase in carbonates. The CSBS tested exhibited great variance in their behaviour regarding the properties assessed, although a strong deproteinating effect was registered on dentin for all.