The Influence of Non-Thermal Plasma Treatment on Osseointegration of Endosteal Implants Presenting Decompressing...

Current evidence suggests that achieving the desired level of osseointegration necessitates a hierarchical approach to implant design. This is particularly relevant for osseointegration around implant systems such as those presenting vertical decompression chambers and acid-etched surfaces which could further be augmented by non-thermal plasma (NTP) treatment. Three implant systems were compared in this study: (i) ND (GM Helix Acqua Implant; Neodent^®, Curitiba, PR, Brazil-hybrid, acid-etched thread design treated with isotonic sodium chloride solution), (ii) Sin (Epikut Plus; S.I.N. Implant System, São Paulo, Brazil-V-shaped, acid-etched thread design treated with nano-hydroxyapatite), and (iii) Mp (Maestro; Implacil De Bortoli, São Paulo, Brazil-buttress, acid-etched thread design with decompressing vertical chambers). The ND and Sin implants were used directly as supplied by the manufacturer. For the Mp implants, the manufacturer-supplied surface was subjected to supplemental acid etching with 37% hydrochloric acid followed by Argon-based NTP treatment administered with a pulsed plasma generator prior to implantation into the iliac crest of n = 12 adult female sheep. Histomorphometric analysis was conducted at 3- and 12-week post-implantation (n = 6 sheep per time point) to assess bone-to-implant contact (BIC) and bone area fraction occupancy (BAFO). After 3 weeks in vivo, the healing chambers of all implant groups consisted predominantly of newly forming woven bone. By 12 weeks, bone maturation was observed, with the presence of remodeling sites and some areas of well-organized lamellar structures occupying the healing chambers. At both 3 and 12 weeks, the Mp implants demonstrated significantly higher BAFO values relative to ND (p = 0.015 and p = 0.008, respectively). The combination of vertical healing chambers, acid etching, and NTP treatment promoted early vascular infiltration and sustained bone deposition.