Evolutions in Microstructure and Properties of Cu-Ni-Si-Mg-Mn Multi-Element High-Solute Alloy During a Short-Time...

To obtain ultrahigh strength Cu alloy strip for board-to-board connectors, a CuNiSiMgMn multi-element high-solute alloy was designed, and high-temperature short-time solid solution was utilized to optimize the properties of this alloy. The evolution in microstructure and properties of the cold-rolled CuNiSiMgMn alloy strip during high-temperature short-time solid solution, aging, and further cold-rolling are investigated. The results reveal that there are high-density Ni_xSi precipitates and deformation defects in the original cold-rolled CuNiSiMgMn alloy strip. During a solid solution at 1000 °C, recrystallization primarily occurs between 15 and 30 s, while precipitate decomposition starts at a solid solution time of ~30 s and is almost complete 10 s later. With further increase in the solid solution time, the grain size of the alloy grows rapidly, but the residual precipitate particles exhibit little change. Upon aging at 500 °C for 2 h and a further 80% cold-rolling, nano-sized precipitates are formed, yielding high-strength alloy strips. The 80% cold-rolling increases the microhardness by 12% and decreases the electrical conductivity by 3% IACS. The strip solid solution-treated for 35 s exhibits the maximum strength, with a tensile strength of >950 MPa and a conductivity of >30% IACS. Further extension of the solid solution time decreases both the tensile strength and elongation. This work clarifies the critical time of recovery, recrystallization, and precipitate decomposition of the CuNiSiMgMn alloy during high-temperature solid solution and provides guidance for industrial production.