Preparation and Synergistic Activation Mechanism of Cemented Backfill Materials Utilizing MSWI Fly Ash and...

A low-titanium-slag-based multi-solid-waste cementitious system was developed for cemented paste backfill. The cementitious binder was prepared from low-titanium slag (LTS), steel slag (SS), municipal solid waste incineration (MSWI) fly ash, and flue gas desulfurization gypsum (FGDG), while lead-zinc tailings were used as the aggregate for backfill materials preparation. The activation of low-titanium slag, proportion optimization, and strength development mechanisms were systematically investigated. Mechanical grinding effectively activated low-titanium slag, and its activity index reached 108% after 90 min of grinding at 28 d. Steel slag alone could not fully activate low-titanium slag in the ternary system, whereas the incorporation of MSWI fly ash significantly enhanced the synergistic activation effect. The quaternary system with 40% MSWI fly ash replacement showed higher cumulative heat release and better later-age strength. The optimum backfill proportion was a solid mass concentration of 81% with a binder-to-tailings ratio of 1:4, yielding a 28 d compressive strength of 11.07 MPa with satisfactory flowability and setting behavior. Microstructural results indicated that the continuous formation of ettringite and gel phases promoted pore refinement and matrix densification. Moreover, the leaching concentrations of Pb, Zn, Cr, and soluble Cl were all below the relevant groundwater quality limits. These results demonstrate a feasible route for the high-value co-utilization of low-titanium slag and MSWI fly ash in cemented backfill materials.