Synergistic Stress-Corrosion Cracking of S135 Drill Pipes Induced by Sulfide-Chloride Drilling Fluid

As a key component in oil drilling, drill pipes are prone to failure in harsh operating service environments. Multiple severe cracks were identified in the S135 drill pipes following field service, with partial crack extensions of ~1 mm detected at the thread roots penetrating into the pipe wall, posing critical threats to structural integrity. This study investigated the failure mechanisms of the drill pipes and examined the potential effects of dynamic rotation on corrosion-assisted cracking. The results showed that this failure was close to the combined results of corrosion and torque. Cl^- and S^2- in the drilling fluid were the main sources of corrosive substances. Cl^- preferentially accumulated on the drill pipe surface, initiating localized pitting corrosion. Under applied stress, these surface pits exacerbated local stress concentration. The synergistic action of S^2- then promoted the transition from pitting to stress corrosion cracking. Regarding the corrosion stage, the rotational state of the drill pipe will affect the drilling fluid's corrosion results. The mud deposition during rotation leads to severe intergranular corrosion, which further causes material peeling. Dynamic rotation at 60 r·min^-1 increased the corrosion rate to 0.55 mm·a^-1 after 216 h of immersion, 41% higher than under static conditions, while maximum corrosion depth increased from 8.43 μm to 13.86 μm. These results indicate that rotational motion accelerates corrosion-assisted cracking.