Assessment of HIPIMS-Deposited TiN Nanostructured Thin Films as Hydrogen Permeation Barriers on Carbon Steel

Hydrogen embrittlement (HE) represents a critical degradation mechanism in carbon steel components operating in hydrogen-rich environments, such as those encountered in clean energy and petrochemical applications. This study evaluates the hydrogen permeation barrier performance of titanium nitride (TiN) nanostructured thin films deposited by High-Power Impulse Magnetron Sputtering (HiPIMS) on SAE 1020 carbon steel substrates. Electrochemical permeation measurements were performed using the Devanathan-Stachurski dual-cell methodology in accordance with ASTM G148 and ISO 17081 standards. Key hydrogen transport parameters quantified include the effective diffusion coefficient (D_eff), lag time (t_lag), and steady-state hydrogen oxidation current density. The TiN/carbon steel composite system exhibited t_lag = 570 s, D_eff = (2.68 ± 0.09) × 10^-10 m² s^-1 and a steady-state hydrogen oxidation current density of 21.5 µA cm^-2, corresponding to a permeation reduction factor (PRF) of 2.32 and a barrier efficiency of η = 56.9%. The superior barrier performance is attributed to the dense, low-defect microstructure characteristic of HiPIMS deposition. These results validate HiPIMS-deposited TiN as a robust hydrogen diffusion barrier, with the established performance metrics providing quantitative benchmarks for the design of hydrogen-resistant coatings in energy applications.