Structure-Property Relationships in PHB-Based Copolymers and PHB/PLA Biocomposites Modified with Hydroxyapatite and...

The challenge of substituting bone defects necessitates the search for effective biomaterials based on biopolymer composites with biocompatible fillers. A promising approach in bone tissue engineering is the use of regenerative scaffolds based on polyhydroxyalkanoates (PHAs), specifically poly(3-hydroxybutyrate)-P(3HB), which are characterized by high biocompatibility and osteoinductive potential. In this study, we evaluate the changes in the mechanical, thermal, and morphological properties of P(3HB) within P(3HB)-copolymers/HA, P(3HB)/CS, P(3HB)/PLA/CS, and P(3HB)/PLA/HA composites. These materials, containing various filler contents (up to 70 wt.% of HA-hydroxyapatite or CS-chitosan), were obtained using melt extrusion compounding. It is shown that the modification of biopolymer matrices promotes a decrease in melting temperature, improvement of mechanical characteristics, and an increase in material elasticity. At high filler concentrations, nanoparticle agglomeration and a deterioration of physical-mechanical properties were observed. It was established that a content of 10-20 wt.% of nano-hydroxyapatite and chitosan is optimal, as these composites most closely match the mechanical properties of bone tissue. The results obtained indicate the high potential of the developed nanocomposites for the creation of biodegradable implants in reconstructive orthopedics.