Effect of Cooling Methods on CFRP-Concrete Bond Behavior After High-Temperature Exposure: An Experimental Study

Concrete structures are highly vulnerable to fire exposure, which accelerates the degradation of mechanical properties and may lead to partial or total structural failure. Externally bonded carbon fiber-reinforced polymer (CFRP) systems are widely used for post-fire strengthening; however, the bond behavior at the interfaces between CFRP and fire-damaged concrete, particularly under different cooling conditions, is not yet fully understood. In this study, the bond behavior was investigated experimentally and theoretically. Double-lap joint tests of thirty-nine specimens were conducted, including three unheated control specimens and thirty-six specimens exposed to temperatures of 200 °C, 400 °C, and 600 °C for durations of one and two hours. Two cooling methods, natural air cooling and water cooling, were applied prior to CFRP bonding. The results indicated that bond strength increased under exposure conditions of no more than 400 °C, whereas a significant reduction was observed at 600 °C. Water cooling resulted in lower bond strength compared with air cooling, while longer exposure durations improved bond performance under certain thermal conditions. The reasons behind the phenomena were analyzed in detail. Based on the experimental results, an analytical model for predicting the bond strength at the interfaces between fire-damaged concrete and CFRP sheets was developed. The model can account for the effects of peak temperatures, exposure durations, and cooling methods, and demonstrated high predictive accuracy (R² = 0.94). The findings provide valuable insight into CFRP-concrete interaction after fire exposure and offer practical guidance for the assessment and rehabilitation of fire-damaged concrete structures.