Impedimetric Analysis of the Photocatalysis-Assisted Response of Patterned TiO₂|ITO Electrodes Exposed to Artificial...

We report the fabrication and electrochemical characterization of TiO₂-based impedimetric sensors for the analysis of artificial sweat compositions. Two-electrode topologies were patterned on indium tin oxide (ITO) substrates: an interdigitated electrode (IDE) configuration and a Hilbert fractal electrode (HFE) geometry. TiO₂ thin films with thickness up to 350 nm were deposited by dip-coating and evaluated as photoactive sensing layers. The impedimetric response of the sensors was investigated by electrochemical impedance spectroscopy in artificial sweat with composition varied in terms of ionic content (0-100 mM Na⁺) and organic content (2.5-30 mM lactic acid and 5-50 mM urea). Regardless of TiO₂ thickness, the high-frequency response is predominantly governed by electrode topology, with the HFE design exhibiting up to 2.5-fold higher modulation compared to the IDE configuration. Under UV illumination, a low-frequency, photo-assisted response emerges, influenced by the TiO₂ layer thickness and primarily sensitive to the organic components of the solution, particularly lactic acid. These results suggest that frequency-resolved impedance measurements in TiO₂|ITO structures may enable partial differentiation between ionic conductivity and organic contributions in sweat, providing a promising basis for multi-parameter sweat analysis.