Theoretical Study on the Formation Mechanism of Ti(C,N) Inclusions and Titanium Content Control in High-Grade...

High-grade non-oriented silicon steel is a critical material for new energy vehicles and energy-efficient appliances due to its superior magnetic properties. However, these properties are significantly degraded by non-metallic inclusions, particularly Ti(C,N). This study employs integrated thermodynamic and kinetic calculations to systematically analyze the formation and growth mechanisms of Ti(C,N) inclusions in high-grade non-oriented silicon steel, trace the sources of [Ti], and propose targeted theoretical control strategies. Results indicate that Ti(C,N) inclusions do not precipitate above the liquidus temperature (1779 K). During solidification, microsegregation enriches Ti, C, and N; however, only TiN precipitates in the final stage as its ion product exceeds the solubility limit, whereas TiC remains undersaturated-findings valid within the present composition window and modeling framework. Inclusion size is governed by cooling rate and initial Ti/N content, where higher cooling rates yield finer inclusions and lower Ti/N content suppresses precipitation. Titanium originates from primary sources (raw materials and alloys) and secondary sources (decomposition or reduction of TiO₂ in slag/refractories). Therefore, mitigating [Ti] requires strictly limiting primary input and suppressing secondary formation through optimized process control, such as reducing BOF slag carryover, lowering refining temperature, and controlling [Al] content.