The right type and quality of aggregates are crucial for concrete as they significantly influence its properties, mix proportions, and cost-effectiveness. If different sources are available for sand, the commonly used fine aggregate in concrete, the selection of sand is primarily based on its gradation.
The grading, or particle-size distribution, of sand is determined using sieve analysis, with standard sizes ranging from 150 μm to 10 mm (ASTM No. 100 sieve to 3⁄8 in. sieve). Sand is sampled...

Deleterious substances in aggregates can be detrimental to the quality and durability of concrete. These substances include organic impurities like loam, which interfere with cement hydration and are usually present in the sand. These prevent a good bond between aggregate and cement paste. Organic impurities can be detected using the colorimetric test, where the darkness of a solution after agitation indicates the level of organic content.
Another type of impurity is clay and fine material that...

The specific heat capacity of a substance refers to the energy required to increase the temperature of one gram of that substance by one degree Celcius. Specific heat capacity is often represented in calories (cal), grams (g), and degrees Celsius (oC), but can also be expressed in joules (J), kilograms (kg), and Kelvin (K), among other units.
For example, increasing the temperature of one gram of water by 1°C requires one calorie of heat energy and can be written as 1 cal/g-°C, or 4186 J/kg/K.

The fineness modulus (FM) of aggregate is a numerical index that measures the coarseness or fineness of the particles. It is calculated by adding the cumulative percentages of aggregate retained on each of a specified series of sieves and dividing the sum by 100.
Consider performing sieve analysis on sand through a set of ASTM sieves. The weight of aggregate retained in each sieve and pan placed at the bottom is recorded, as given in Column B of Table 1.
To determine the fineness modulus of...

Concrete exposed to seawater can undergo degradation like the dissolution of ettringite and gypsum, increasing the material's porosity and decreasing its strength. In contrast, the crystallization of salts within the concrete's pores can cause expansion, particularly above the waterline where evaporation occurs. Nonetheless, this expansion only happens when seawater, enabled by the concrete's permeability, manages to infiltrate the structure.
Concrete in areas between tide marks, which undergo...