Formulation and Performance Evaluation of Epoxy Sealant Systems for Double-Shell Tank Bottom Refurbishment

The performance of epoxy sealants used in the refurbishment of double-shell tank (DST) systems requires balancing processability, thermomechanical stability, and adhesion to cementitious substrates. This study incorporates Heloxy 8 as a reactive diluent into Westlake 862 epoxy to tailor workability and cured-state properties. Rheological time-sweep analysis demonstrates that increasing the diluent content significantly reduces complex viscosity and extends workability, thereby improving pumpability and flow for large-area applications. However, the targeted 2-hour processing window is not fully achieved. Differential scanning calorimetry (DSC) confirms that all formulations cure at room temperature to glass transition temperatures (T_g ) at least 20 °C above the maximum DST operating temperature (27 °C), thereby ensuring service in the glassy regime. Dynamic mechanical analysis (DMA) reveals formulation-dependent reductions in tan delta and increases in storage modulus, indicating increasingly elastic and mechanically stable networks with diluent incorporation. Pull-off adhesion testing shows that modified formulations (70-90% Westlake epoxy) exhibit significantly higher adhesion strengths than the unmodified system. Grout cohesive failure indicates that interfacial bonding exceeds substrate strength. Collectively, these results demonstrate that controlled reactive diluent incorporation enables optimization of processing behavior, interfacial adhesion, and thermomechanical performance, supporting the suitability of the modified epoxy systems as durable sealant layers for cementitious barrier applications in hazardous waste containment infrastructure.