Influence of Transition Metal Ion Contaminants on the Performance of Amine-Based Solid Sorbents in Direct Air Capture

Amine-functionalized solid sorbents are a class of sorbent materials proposed for direct air capture (DAC) of CO₂, yet their long-term performance is susceptible to degradation under realistic operating conditions. Many amines are not thermodynamically stable in air, and amine sorbents oxidize while in use during DAC temperature swing adsorption processes. In this study, we investigate the role of transition metal ion contaminants, specifically Cu²⁺, Fe²⁺, and Ni²⁺, on the oxidative degradation of poly(ethylenimine) (PEI)-impregnated SBA-15 sorbents. By introducing metal ions via different modes mimicking both synthesis-related impurities and impurities derived from environmental exposure, we systematically evaluate sorbent stability after exposure to dry air at an elevated temperature. Thermogravimetric CO₂ uptake measurements reveal that even trace levels of Cu and Fe (as low as ∼4 ppm) can lead to measurable sorbent deactivation after oxidative aging, despite negligible loss in the performance of the control samples. In situ infrared, UV-vis, and X-ray photoelectron spectroscopies indicate that these metals catalyze radical-driven oxidation pathways, altering the chemical structure of the sorbent and accelerating degradation. Our findings underscore the need to account for trace metal contamination during DAC sorbent synthesis and deployment and highlight the importance of environmental contamination pathways.