Innovative plasma-polymerized bilayer coating featuring a citronellal-based antimicrobial layer and a...

The development of active food packaging materials with controlled antimicrobial release is essential for improving food safety and extending shelf life. In this study, a plasma-polymerized bilayer coating was developed on polylactic acid (PLA), consisting of a citronellal-based antimicrobial layer (∼505 ± 13 nm) and a polycaprolactone (PCL) barrier layer with controlled thicknesses of 30 nm and 55 nm. Surface characterization confirmed successful deposition and partial preservation of citronellal functionality. Release studies demonstrated a strong burst release for the pristine citronellal coating, with most citronellal released within the first day, whereas the bilayer systems significantly reduced and controlled the release. For example, in 95% ethanol after 10 days, citronellal release decreased from 2724.4 μg/L (no barrier) to 210.9 μg/L (30 nm PCL) and 39.1 μg/L (55 nm PCL). Antimicrobial tests in vacuum-packed pork sausage showed that the pristine coating provided strong initial reductions (up to 2.93 log CFU/mL for Listeria monocytogenes (L. monocytogenes) and 2.48 log CFU/mL for lactic acid bacteria (LAB) by day 5), followed by regrowth due to depletion. In contrast, bilayer coatings enabled sustained antimicrobial activity over 11 days, achieving reductions of 3.97 and 3.37 log CFU/mL (30 nm PCL) and 3.14 and 2.09 log CFU/mL (55 nm PCL) for L. monocytogenes and LAB, respectively. The 30 nm PCL layer provided the optimal balance between release rate and antimicrobial efficacy. These results demonstrate that the PCL barrier effectively modulates citronellal release, enabling prolonged antimicrobial activity. The developed bilayer system represents a promising approach for controlled-release antimicrobial food packaging applications.