Aminated Graphene as an Advantageous Filler for Polymer Composites with a Segregated Structure

Conductive polymer composites with a segregated structure are a promising route to obtaining electrically active materials at low filler loadings. In this work, aminated graphene (AmG) was used as a functional conductive filler for the fabrication of composites with a segregated structure based on polyvinyl chloride (PVC) and poly(vinylidene fluoride-co-tetrafluoroethylene) (P(VDF-TFE)). AmG was comprehensively characterized by electron microscopy, core-level and near-edge spectroscopy, optical spectroscopy, and electrical measurements. The synthesized AmG contained 14.34 at.% nitrogen, with amines accounting for 81.44% of the nitrogen-related spectral intensity, corresponding to an amine concentration of 11.78 at.%. AmG also exhibited a restored π-conjugated network, intrinsic conductivity of 20-33 S/cm, and a crumpled-flake morphology favorable for interfacial contact with polymer particles. At a filler loading of only 1 wt.%, the segregated composites reached electrical conductivity up to 1.3-1.4 × 10^-4 S/cm, exceeding those of the unfilled polymers by seven orders of magnitude. At 11 GHz, the AmG-filled P(VDF-TFE) composite showed 15.1 dB attenuation for a theoretical thickness of 30 mm, transmitting no more than 3% of the incident radiation. These results identify AmG as a functional conductive filler for segregated electrically conductive polymer composites and demonstrate that the combination of amine-containing surface chemistry, restored electrical conductivity, and crumpled morphology enables conductive interparticle network formation in PVC- and P(VDF-TFE)-based composites at only 1 wt.% filler loading.