Development and Performance Assessment of Single- and Double-Layer TbAG:Ce and YAG:Ce Composite Scintillators on...

In this work, we report the fabrication and characterization of single-film and double-film composite epitaxial garnet structures based on single-crystalline films (SCFs) and bulk single-crystal (SC) scintillators for enhanced α-γ discrimination in mixed radiation fields. These composite scintillators consist of TbAG:Ce and YAG:Ce SCFs grown by liquid-phase epitaxy (LPE) on Czochralski-grown Gd₃Ga_2.5Al_2.5O₁₂ (GAGG:Ce) bulk SC substrates. Single- and double-film architectures were designed to optimize the energy absorption and pulse-shape discrimination (PSD) performance for low-penetrating α-particles and high-energy γ-rays. Energy calibration was performed using different γ-ray sources (⁵⁷Co, ⁵¹Cr, and ¹³⁷Cs), enabling the conversion of detector signals to a calibrated electron-equivalent energy scale (keVee). Integration gates were systematically optimized, yielding maximum figures of merit (FOM) of 1.4 for the GAGG:Ce SC substrate, 1.9 for the single-film composite, and 5.0 for the double-film composite, demonstrating a progressive improvement in α-γ discrimination with increasing structural complexity. Two-dimensional PSD density maps reveal well-separated α and γ events, with the highest separation observed for the double-film composite. These results indicate that the engineering of LPE-grown composites provides tunable scintillation decay profiles, enhanced temporal separation, and increased light yields, making them promising candidates for applications such as mixed radiation field detection, dosimetry, and radiation monitoring.