The Failure of Voltage Divider Induced by Insulating Material Degradation Under Coupling Effect of High-Frequency...

This paper systematically investigates the failure characteristics and mechanisms of insulating materials in DC voltage dividers under combined high-frequency voltage and high-temperature conditions via simulations and experiments. The results showed that high-frequency harmonics severely degrade the insulation strength of polypropylene/paper/polypropylene (PPLP) at 10 kHz, in which the bulk breakdown strength of PPLP decreases by over 50%. Furthermore, the surface flashover voltage in oil is reduced by 17.7% under high-frequency voltage alone, and by as much as 51% when white flocculent substances are present in the oil. The dielectric properties of PPLP strongly depend on frequency and temperature, which aggravate the heat accumulation of the divider under high-frequency voltage. Furthermore, the multilayer structure of PPLP introduces deeper trap levels due to interfacial states, which reduce the breakdown strength and flashover voltage of PPLP. Electro-thermal coupling induces a rapid temperature rising to 98 °C at 25 kHz caused by dielectric loss, leading to oil turbidity and white precipitation, consistent with finite element simulations. Consequently, a failure mechanism is proposed as follows: prolonged electro-thermal stress causes chain scission in styrene-containing materials, releasing monomers that repolymerize into white polystyrene deposits. Their porous structure and dielectric mismatch distort the interfacial field, trigger partial discharge, and aggravate surface flashover.