Performance and Synergistic Mechanism of FeSiBCuNb Amorphous Alloy Catalyst for Methylene Blue Degradation

The massive discharge of methylene blue causes severe water pollution, and the development of efficient and stable heterogeneous Fenton catalysts is crucial for wastewater treatment. To address the shortcomings of traditional iron-based amorphous catalysts, such as low activity and poor stability, this study employed Fe₈₀Si₆B₁₀Cu₁Nb₃ five-component amorphous alloy as the catalyst to investigate its catalytic degradation performance, cyclic stability, and catalytic mechanism for MB. Batch experiments, SEM, XRD characterization, and kinetic fitting were combined to carry out the research. The results showed that under the optimal conditions (25 °C, pH = 3, H₂O₂ concentration of 5 mM, catalyst dosage of 0.5 g/L), the catalyst could completely degrade methylene blue within 9 min with a reaction rate constant k_obs of 0.44 min^-1, and the degradation efficiency showed no obvious attenuation after 20 consecutive cyclic degradation runs. After degradation, slight selective corrosion occurred on the catalyst surface, while the amorphous structure of the matrix remained stable. This study confirms that the Cu/Nb dual synergy improves the catalytic performance and stability, clarifies the relevant catalytic mechanism, and provides theoretical and technical support for the design of high-performance iron-based amorphous catalysts and the treatment of dye-containing wastewater.