A Hierarchically Structured Composite Integrating a Biomass-Derived Magnetic Carbon Framework with Various Magnetic...

A lightweight and high-efficiency microwave-absorbing material was developed via an in situ solvothermal pyrolysis strategy by anchoring sphere-like Fe₃O₄ nanostructures onto bamboo-derived porous carbon (BPC). The resulting composites preserve the intrinsic anisotropic honeycomb architecture of bamboo while introducing uniformly distributed magnetic nanoparticles, enabling synergistic dielectric-magnetic loss. Electromagnetic parameters, alongside impedance matching, were successfully modulated through the optimization of precursor concentrations. Of the evaluated materials, BPC-0.9 stood out for its intense attenuation, recording an RL_min of -45.17 dB at a 1.8 mm thickness. Furthermore, a significant effective absorption bandwidth of 6.65 GHz was attained by the BPC-0.6 sample at only 2.2 mm. Several factors contribute to the boosted efficiency, starting with conductive and interfacial polarization losses paired with multiple scattering events. Furthermore, magnetic loss components, encompassing eddy current effects as well as natural and exchange resonances, play a pivotal role in optimizing the material's response. Furthermore, radar cross-section (RCS) modeling reveals a substantial reduction of 19.9 dB·m², verifying the material's viability for real-world stealth technologies. Our findings offer a straightforward methodology for fabricating magnetic carbon structures from biomass with adjustable dielectric responses, underscoring their potential in high-performance energy conversion and low-density microwave absorption.