Polymers that are made up of identical monomer units are called homopolymers. Only one repeating unit is involved in the construction of the homopolymer structure. For example, as depicted in Figure 1, polypropylene is a homopolymer constituted of propylene monomers. Here, the only repeating unit in the polymer chain is propylene.

Synthetic polymers are classified as elastomers, fibers, or plastics based on their crystallinity. Crystallinity, the degree of long-range order in the solid state, influences the mechanical properties (stretching or contracting) of elastomers. Elastomers are flexible polymers that can expand or contract easily upon the application of an external force. They have numerous crosslinks that pull them back into their original shape when stress is removed. Silicones, for instance, are highly elastic...

Introduction
A comparison of the enthalpies of hydrogenation of dienes reveals that conjugated dienes release less heat on hydrogenation, rendering them more stable than their nonconjugated analogs.

Polymers are classified as linear or branched on the basis of their chain architecture. The polymer chains in linear polymers have a long chain-like structure with minimal to no branching at all. Even if a polymer features large substituent groups on the monomer, which appear as branches to the skeleton, it is not considered a branched polymer. A branched polymer contains secondary polymer chains that arise from the main polymer chain. The branching occurs when the polymer growth shifts from...

Copolymers are the products obtained from the polymerization of multiple monomer species. So, in a polymer chain itself, there can be multiple repeating units that come from different monomers. The process of synthesizing a polymer from different monomer species is called copolymerization. When two monomers are involved, the polymer is known as a bipolymer. Polymers with three and four monomers are termed terpolymers and quaterpolymers, respectively. Figure 1 depicts the copolymerization of...

Step growth polymerization involves bi or multifunctional monomers. Bifunctional monomers react to form linear step growth polymers, whereas multifunctional monomers react to form non-linear or branched polymers.
As the step-growth polymerization involves step-wise condensation of monomers, the molecular weight also builds up eventually. Consequently, high molecular weight polymers are obtained at the late stages of the polymerization, where 99% of monomers have been consumed.
The extent of the...